Processing of flame retardant textiles in industries

The term flame retardant is used to describe fabrics which will not support combustion and are self –extinguishing. Fabrics of this type, when involved in an accidental fire would not contribute to spreading the flames. Other descriptions, such as flameproof, fireproof and flame resistant, are either meaningless or misleading. Nearly all fabrics are combustible to some degree. The rate of burning ranges from that of guncotton (nitrocellulose), which burns so quickly that it produces an explosion, to that of asbestos, which is virtually unaffected by the fire.

Figure: The term flame retardant is used to describe fabrics which will not support combustion and are self –extinguishing. 

Flame retardant fabrics can be produced in two ways.

  1. by making them of fibers which do not burn.
  2. by chemically treating the fibers to produce the desired effect.

There was a time originally when such materials could only be produced by employing a chemical finish. However, this can often cause problems, in terms of the durability of the process and its impact on the environment. Strict controls are required to achieve consistency and problems arise likewise with the final look of the material. Even where the flame–retardant quality is guaranteed over a certain number of washes, there can be no certainty of the effectiveness of the procedure, as it is practically impossible to monitor the number of washes in practice.

All such difficulties are avoided by the use of permanently modified chemical fibers. The polymer was invented in 1974. The development of staple fibers and filament took place in 1976-79. It was introduced in the USA in 1979 and in Europe in 1980. The permanent flame retardant properties were due to the organic phosphorous compound incorporated into the polymer chain. As it was a low-level modification the textile properties of the polymer remain unchanged.  Fire Retardant polyester fiber came to India by Hoechst AG, Germany by the trade name of Trevira CS (CS stands for Comfort and Safety).

From the outset, there was also a large role for home textiles, today the most important sector for Trevira. the product range extends from drapes, decorative and upholstery fabrics, to carpet fibers. Yet here too the portfolio began to change towards specialties early. In 1980 one such was Trevira CS, a flame retardant fiber, which from its launch recorded ever-rising growth rates and is today the star product of the company. With over 1000 flame retardant Trevira CS fabric collections for the home textiles sector worldwide, Trevira is the market leader in this segment. Since then the range of flame retardant fibers and yarns has undergone a steady flow of changes and innovations.

In 2004, Reliance crossed another milestone in its polyester journey when it acquired Trevira GmbH, an erstwhile division of the German giant Hoechst AG a leading producer of branded polyester fibers in Europe.

Specific moisture absorption of Trevira is around 0.4 % at 20 deg c and 65 % RH. It can however be made considerably higher by the hydrophilic surface of the material and the capillary effect between the fibers. Moisture penetration is very high, thus releasing humidity, something very important for instance for sitting comfortably. Trevira cs has been tested to German, American and Japanese health standards and been adjudged non-toxic, not allergenic or mutagenic and non-irritant. The Eco-Tex 100 test confirms that Trevira CS is free from harmful substances. Trevira CS has three flame retardant mechanisms it melts away from the flame, absorbing ignition energy. Flame retardant groups quench reactive species, chain reactions cannot propagate. The polyester modification created by Trevira performs a very important function. Within a flame, highly charged elements called radicals are released which rapidly propagate more flames. The Trevira modification captures and neutralizes the radicals before they can propagate more flames. Trevira belongs to the polyester group of fibers, which are rendered permanently flame-retardant by the inclusion of a small proportion of a phosphorous–organic component. They display all the typical properties of polyester fibers and offer industry and consumers considerable advantages. Hoechst (Germany) gave the license only to Rajasthan Spinning and Weaving Mills, Gulabpura (Rajasthan) to use this fiber in India. Trevira supplies 100% Trevira flame retardant fibers or filament yarns.

Trevira CS fabrics are made from flame retardant fibers and used therefore in the home textile and contract furnishing sectors. They are flame retardant to all appropriate fire protection requirements and produce only slight amounts of smoke fume. For the first time, the flame retardant qualities combine with bioactive properties to also provide safety from microbes. These qualities are not lost by cleaning, aging, or wear. Trevira cs is easy to care for light, fast, comfortable and kind to the skin. Trevira CS is used in hotels, and hospitals, in offices and event rooms and principally where people are traveling on aircraft, buses trains and at sea.

Following are the advantages of using Trevira

  1. Outstanding running properties in spinning and twisting.
  2. Very good processability, high yarn uniformity and tenacity for weaving, circular and warp knitting.
  3. Excellent dyeability using a variety of methods, and environmentally friendly finish processes give crease-resistant fabrics with good shape retention.
  4. Good hard–wearing properties.
  5. Easy–care.
  6. Outstanding light fastness.
  7. Permanent flame retardance.

Following are the processes involved in making fire retardant textiles.

  1. Spinning
  2. Bleaching
  3. Dyeing
  4. Finishing
  5. Printing

The above process are discussed below.

  1. Spinning – is classified into two types
  • Grey CS yarn
  • Dyed CS yarn

Grey fiber is normally available in 1.4 D x 44 mm. the spinning is done in the same manner as 100 % normal polyester fiber. the process is as follows.

Blow room – Carding – Draw frame – Simplex – Ringframe – Winding – TFO – Packing.

The grey yarn goes for weaving and making the soft package for yarn dyeing.

Secondly, the dyed fiber is received from Dyehouse. The dyed fiber is sprayed with LV 40 and 2152P and conditioned for 16 hrs. Then it follows a similar route in spinning as prescribed for 100 % dyed normal polyester fiber. The dyed yarn is sent to weaving /knitting.

Flame retardant Trevira CS spinning yarns can be used in any spinning process, resulting in outstanding with Ring spinning, OE –rotor and Airjet spinning, as well as with carded yarns and worsteds. A variety of effects is possible for which the product range includes dull, semi-dull and bright types. Extremely fine three-cylinder yarns are used in delicate fabrics, decorative materials and bed linens.

The OE –rotor yarns with a flat, soft structure form the basis for decorative fabrics, vertical blinds and mattress materials. The current demand for soft, transparent and bright yarns is particularly met by filament yarns of the high–capillary type for drapes and decorative fabrics. Degree of fineness range from 50 dtex with delicate goods through to 3000 dtex for cover fabrics with high wear and light fastness properties. with a false twist, yarn one can achieve light but bulky weaves.

The wide range of fire-retardant Trevira spun yarns enables spinners to offer a complete collection of yarns. They have a quality which is not only ideal for their purposes but is fire-retardant as well. The range comprises degrees of fineness for practically every application; from the finest ( 1.3 >1.7 dtex) for delicate fabrics right through to the extremely coarse ( 13 dtex ) for carpets.

  1. Bleaching – Bleaching is not required before dyeing dark and medium shades. It is almost white. But in the case of clear and pastel shades bleaching with peroxide is required before dyeing.
  2. Dyeing – there are four types of dyeing
  • Filament yarn dyeing
  • Spun yarn dyeing
  • Loose staple fiber dyeing
  • Fabric dyeing
  • Filament yarn dyeing– normally 165 dtex is used in filament dyeing. soft package of 700-800 gms is made on perforated poly propylene tubes by the precision soft winding machine having an overfed attachment. Then it is dyed in HTHP Dyeing machines at the temperature of 120 deg c. for 30-45 mins depending on shades.

It is Hydroextracted in Dettin package Hydroextractor. It is dried in RF Dryer. It is reminded on a paper cone. The dyed package goes for Weaving or Knitting. The principal applications for flat yarns are in curtains and decorative fabrics, irrespective of whether these are false twists, jet –tex, jet-tweed, multicolor, or chenille yarns. A further possibility involves the use of texturized filament yarns, where a very wool-like character can be achieved with especially air–textured types for furniture fabrics.

  • Spun yarn dyeing– Similarly spun yarn is made in various counts ranging from 2/5, 2/8,2/12, and 2/20. 2/24.,2/30.2/50. Then a soft package is made on ps Mettler or SSM winding machines. Package weight is 900 gms to 1 kg. It is loaded in HTHP dyeing machines. It is dyed at 120 deg c. The rest process is as above. An even wider range of design perspectives is opened up by combining filament and fiber yarns. employing fancy yarns, such as knit-deknit types, produces striking designs. Jet-tex and tweed types are mainly used as upholstery and decorative material and as wall coverings.
  • Loose staple fiber dyeing – Normally 1.7 d x 44 mm Trevirs CS fiber is available for dyeing. The CS fiber is loaded in the carrier. Then the loaded carrier goes into the HTHP Dyeing Machines. It is dyed at 120 deg c. at a pH of 4-5 with a leveling agent like Lyogen DFT (of Clariant) is added. Dark shades are reduction cleared with Caustic Soda and Sodium Hydrosulphite. (1 GPL and 2 GPL respectively). Then hot wash at 85-90 deg c. Then acid is neutralized by acetic acid. Then Antistatic Agent Sapcotex F (Henkel)– 0.4 % (o w g) Then the carrier is offloaded. The dyed fiber goes for Hydroextraction. Then it is dried in RF Dryer / Steam Dryer.

Total Dyeing time takes about 4-4.5 hrs.

With a 40 deg c wash, there are no discernible differences between normal polyester and Trevira CS fibers. At 60 deg c with the same dyeing similar values are achieved on flame retardants as on non-modified types.

  • Fabric Dyeing – Trevira CS fabric is dyed in jet dyeing machines. The process is followed as above. After dyeing it is squeezed and dried in stenter at a lower temperature of 140 deg c to 150 deg c. Dispersion dyes take on fire–retardant somewhat faster than the corresponding normal polyester types. Due to this light shades can be dyed at boiling temperature without adding a carrier. Medium to dark shades are dyed without a carrier at a maximum temperature of 120 deg c. Disperse dyes used are high-energy dyes from Dystar, Germany known as Dianix FG dyes or Foron RD dyes from Clariant, Basle. In raw white for piece dyeing or as multicolored yarns, flame retardant textiles can be made in all desired qualities. In general dyeing with colored and patterned fabric results in adequate wash fastness. Preliminary tests are recommended however as there is a possibility of staining adjacent material. Dyes on Trevira cs are fast to washing at boiling temperatures in bright shades and with selected dyestuff. Chlorine –a fast finish is possible with the appropriate dyestuffs. Boiling is not recommended for drapes and decorative fabrics.
  • Finishing – Selection of softeners is very critical. it has to be seen there is no negative effects on burning behavior. Leomin ni of Clariant is the recommended softener to be used for cs fabrics in the dose level from 1 to 5 GPL. Trevira CS materials may be coated with PVC or polyurethane. An antimicrobial or fungicide finish is possible with Dodigen (from Clariant) or Afrotin LC (the Schill and Seilacher company). whilst maintaining the relevant fire category.

Whilst being processed Trevira cs fabrics can be exposed for brief periods to temperatures above 210 deg c. where they are exposed to temperatures for longer times, we recommend a maximum of 150 deg c in dry atmospheres and 100 deg c in humid conditions. With flame–retardant types in deep shades the fastness properties reduce by ½ degree as compared to dyes on normal types.

  • Printing – Pigment printing is not recommended for Trevirs CS fabrics because the use of binder and thickeners influence the flame retardant properties negatively.

 Transfer printing can be done on Trevira CS fabrics. Any papers printed with dispersion dyestuffs can be employed. Checks should first be made to ensure the Light Fastness of the dyestuffs involved is adequate. Varnish should not be used as part of the residue may adhere to the fabric in printing and exercise a negative effect of the flame-retardant behavior on Trevira CS material

Wear properties of Trevira CS fabrics

  1. Stability – very good.
  2. Abrasion resistance – > 60,000 Martindale
  3. Durability – very good.
  4. Light- fastness – 7-8.
  5. UV-Stability Hrs – 80 % (1400 Xenotest)
  6. Washability – 60 deg c.
  7. Stain removal – very good.

Trevira CS fabrics satisfy all the relevant and important fire protection standards.

If anyone has any feedback or input regarding the published news, please contact: info@textiletoday.com.bd

Related posts

ProGARM launches flame-retardant face mask

Textile Today

Flameproofings installed a state of the art BRÜCKNER coating plant

Textile Today

Ergonomics and comfort central to flame retardant apparel industry: Fact.MR study

Textile Today

Latest Publications

View All